Two-component zinc epoxy coating with high pure zinc content.

E-Primer I EP-173

ZINC EPOXY PRIMER

Two-component zinc epoxy coating with high pure zinc content.

Category: Tags: , ,

Description

• Excellent adhesion to ferrous and non-ferrous metals (aluminum, hot-dip galvanized surfaces);
• Heat resistance of the film up to 200°C;
• Usable at low temperatures (down to –5°C);
• Resistant to solvents, acids, bases, and their vapors;
• Compatible with various organic topcoats.

Purpose

Used for the protection of industrial equipment, pipes, tanks, and metal structures against atmospheric corrosion and heavy chemical exposure. Characterized by exceptional strength and wear resistance. Suitable for metal elements, structures, and equipment including bridges, tanks, pipelines, production facilities, port equipment, and other heavy industry objects up to C5 (ISO 12944-2).

ColorAccording to sample/RAL catalog
Gloss0 - 5 %
AppearanceThixotropic mass
Theoretical consumption rate250 g/m2 for a 60 μm dry film
Density2.55 kg/l
Solid content62 %
Shelf life36 months
VOC340 g/l
Drying Stage20°C30°C
Touch dry 45 minutes 35 minutes
Fully dry 4 hours 3 hours 15 minutes
Fully cured 24 hours 24 hours
Recoat interval after 3 hours after 3 hours
Pot life 8 hours 7 hours

Related products

  • Read more

    THINNER

    EP-500

    Used for thinning epoxy resins, primers, paints, varnishes, and all Bulmat cold galvanizing products. Speeds up drying and reduces the time needed for applying subsequent coats. Characterized by a mild and non-intrusive odor. Excellent for cleaning paint brushes, rollers, spray guns, and pumps after use. Also suitable for degreasing metal surfaces.