E-Guard I ЕP-172 АC HS

E-Guard I ЕP-172 АC HS

EPOXY COATING

A high-build, two-component epoxy coating with a high content of anti-corrosion additives (zinc phosphate) and high solids content, designed for long-lasting protection of metal surfaces.

Category: Tags: , , ,

Description

• Excellent adhesion to ferrous and non-ferrous metals (aluminum, hot-dip galvanized surfaces);
• Resistance to scratching and wear;
• Heat resistance of the film up to 200°C;
• Usable at low temperatures (down to –5°C);
• Compatibility with various organic-based top coatings;
• Ability to apply in thick layers without sagging – up to 300 μm;
• Forms water-and vapor-impermeable coating;
• Can be used as a one-coat system to reduce primer and paint costs;
• Coating with high solids content and low consumption per unit thickness.

Purpose

This coating is used for protecting industrial facilities, pipelines, storage tanks, and metal structures from atmospheric corrosion and heavy chemical loads. It is distinguished by exceptional strength and abrasion resistance. It can be applied as a standalone coating in operating environment C3 (ISO 12944-2) or as an intermediate/topcoat in anti-corrosion systems for severe environments C4/C5 (ISO 12944-2). It is suitable for use at low temperatures (down to –5°C).

ColorAccording to sample/RAL catalog
Gloss50 - 75 %
AppearanceThixotropic mass
Theoretical consumption rate99 – 111 g/m2 for a 60 μm
Density1.39 – 1.56 kg/l
Solid content84 %
Shelf life36 months
VOC249 g/l
Drying Stage20°C30°C
Touch dry 2 hours 1 hours 45 minutes
Fully dry 8 hours 7 hours
Fully cured 24 hours 18 hours
Recoat interval after 8 hours after 8 hours
Pot life 6 hours 5 hours 10 minutes

Related products

  • A high-build, two-component epoxy coating with a high solids content, designed for long-lasting protection of metal surfaces.
    Read more

    EPOXY COATING

    E-Guard Plus I ЕP-1722 АC HS

    A high-build, two-component epoxy coating with a high solids content, designed for long-lasting protection of metal surfaces.

  • Двукомпонентно епоксидно бързосъхнещо покритие с високо съдържание на бариерни съставки (MIOX – слюдест железен оксид)
    Read more

    EPOXY COATING

    E-Guard Plus I ЕP-1721 АC HS

    A two-component, fast-drying epoxy coating with a high content of barrier additives (MIOX – micaceous iron oxide) designed for the protection of surfaces on ferrous and non-ferrous metals. It offers excellent anticorrosion properties.

  • Read more

    THINNER

    EP-500

    Used for thinning epoxy resins, primers, paints, varnishes, and all Bulmat cold galvanizing products. Speeds up drying and reduces the time needed for applying subsequent coats. Characterized by a mild and non-intrusive odor. Excellent for cleaning paint brushes, rollers, spray guns, and pumps after use. Also suitable for degreasing metal surfaces.

Related products

  • Read more

    FAST-DRYING ALKYD COATING

    A-Power 2-in-1 Rapid I AS-1211

    Single-component, self-priming, fast-drying coating for industrial use with a high content of anti-corrosion additives (zinc phosphate). Reduces application costs by serving both as a primer and a topcoat.

  • Read more

    FAST-DRYING ALKYD COATING

    A-Power 3-in-1 Rapid I AS-1212

    A single-component, self-priming, fast-drying coating for industrial use with a high content of corrosion protection additives (zinc phosphate) and active ingredients that convert corrosion. This coating simultaneously functions as a rust converter, primer, and topcoat, thereby significantly reducing coating costs.

  • Read more

    FAST-DRYING INDUSTRIAL TOPCOAT

    A-Power Rapid I 131

    A fast-drying, single-component finish coating on an alkyd base characterized by exceptional strength.

  • Read more

    FAST-DRYING INDUSTRIAL COATING

    A-Power 2-in-1 Rapid I 1311

    A single-component, self-priming, fast-drying coating for industrial use with a high content of anticorrosion additives (zinc phosphate). This coating lowers overall costs by serving as both a primer and a topcoat.